Stellite 6/ Stellite 6B/ Stellite 12 valves seat Ring/ Sleeve

Stellite 6/6B Valves Seat Ring/ Sleeve

♦ Material: Stellite Alloys, Stellite 6, Stellite 6B, Stellite 12 ♦ Forms: Ring,  Sleeve  as per clients drawing or specification ♦ Surface: Polished/ Grinding ♦ Tolerance:+/-0.01 mm On OD and ID ♦  Hardness: 38-55 HRC ♦  Standards :AMS 5387 ect

Stellite 6 or cobalt 6 cobalt based alloys produced by centrifugal casting or sand moulding, used in bushings and wear rings to improve wear resistance.

Condition: Casting, stress relief before processing

Heat treatment: stress relief: heat the casting to the minimum 800℃, hold for 1-4 hours slow cooling.

Process: All castings of the same batch shall be of the same quality without pores, pores, hard spots, shrinkage defects, cracks or other harmful defects.Single castings with isolation holes below 0.5 mm are not allowed to be repaired, plugged or welded.

Semi-finished castings for EMS final machining shall be provided in "Machining Inspection Status" to allow casting to be inspected prior to shipment.

Stellite Alloys Chemical compositions and properties (%)

 

Material	C	Mn	Si	Cr	Ni	Mo	W	Co	Fe	P	S	Density(g/cm3)	Hardness(HRC)
Stellite 3	2.0-2.7	1.0	1.0	29-33	3.0		11-14	Bal.	3.0	≤0.03	≤0.03	8.55	51-55
Stellite 6	0.9-1.4	1.0	1.5	27-31	3.0	1.5	3.5-5.5	Bal.	3.0	≤0.03	≤0.03	8.35	38-44
Stellite 12	1.1-1.7	1.0	1.0	28-32	3.0		7.0-9.5	Bal.	3.0	≤0.03	≤0.03	8.40	44-49

Application: Stellite6B alloy is one of the cobalt-based wear resistant Bai alloys, wear resistance and toughness, can adapt to most conditions, a wide range of applications, hardness in 37-45HRC;It is mainly used for chemical wear-resisting plate, wear-resisting rod, steam chemical valve seat, steam turbine blade protection, anti-erosion bushing, hot dip galvanized submerged roller and other parts;Compared with WR6 (Stellite6) WR6B, WR6B has better high temperature wear resistance