♦ Material: Inconel Alloy 600
♦ Size : M10-M120
♦ Grade: AAA Grade
♦ We produce and Supply Inconel 600 bolt, Screw, Nuts as international standards size also can be produce as per clients drawing
Contact Us to Learn More !Inconel 600 is a nickel-chromium alloy used for applications that require corrosion and high temperature resistance. This nickel alloy was designed for service temperatures from cryogenic to elevated temperatures in the range of 1090 C (2000 F). It is non-magnetic, has excellent mechanical properties, and presents the desirable combination of high strength and good weldability under a wide range of temperatures. The high nickel content in UNS N06600 enables it to retain considerable resistance under reducing conditions, makes it resistant to corrosion by a number of organic and inorganic compounds, gives it excellent resistance to chloride-ion stress-corrosion cracking and also provides excellent resistance to alkaline solutions.
Inconel 600 Chemical Composition| Alloy |
% |
Cr |
Fe |
Ni+Co |
C |
Mn |
Si |
S |
Cu |
Ti |
|
600 |
Min. |
14.0 | 6.0 | - | - | - | - | - | - |
0.7 |
|
Max. |
17.0 |
10.0 |
72.0 | 0.15 | 1.0 | 0.5 | 0.015 | 0.5 |
1.15 |
Inconel 600 Physical Properties
| Density | 8.47 g/cm³ |
| Melting point | 1354-1413 ℃ |
| Status |
Tensile strength ksi MPa |
Yield strength Rp 0. 2 ksi MPa |
Elongation As % |
Brinell hardness HB |
| Annealing treatment | 80(550) | 35(240) | 30 | ≤195 |
Round bars/Flat bars/Hex bars, Size From 8.0mm-320mm, Used for bolts,fastners and other spare parts
Supply in welding wire and spring wire in coil form and cut length.
Forging Ring or gasket,size can be customized with bright surface and precision tolerance
Widths up to 1500mm and lengths up to 6000mm,Thickness from 0.1mm to 100mm.
Standards size and customized dimension can be produced by us with small tolerance
Standards size and customized drawing can be produced by us with precsion tolerance
Soft condition and hard condition with AB bright surface, width up to 1000mm
Alloy 600 materials in forms of Bolts,screws,flanges and other fasterners, according to clients specification.
Ni-Cr-lron alloy.solid solution strengthening.
Good resistance to high temperature corrosion and oxidation resistance.
Excellent hot and cold processing and welding performance
A satisfactory heat intensity and high plasticity until 700℃.
Can be strenathened through the cold work.also can use resistance welding,welding or soldering connection.
Good corrosion resistance:
Corrosion resistance to all kinds of corrosive media
Chromium compounds make the alloy have better corrosion resistance than nickel 99.2 (200) alloy and nickel (alloy 201.low carbon) under the condition of oxidation
At the same time the high content of nickel alloy shows good corrosion resistance in alkaline solution and in reduction conditions.and.can effectively prevent the chloride-iron stress corrosion cracking
Very good corrosion resistance in acetic acid.acetic acid. formic acid.stearic acid and other organic acids.and corrosion resistance in.inorganic acid media.
Excellent corrosion resistance in a nuclear reactor in primarv and secondarv circulation use of high purity water
Particular prominent performance is the ability to resist dry chlorine and hydrogen chloride corrosion. application temperature can be up to 650 ℃.At high temperature, the alloy of annealing and solid solution treatment states in air has the very good antioxidant performance and high peeling strength
The alloy also shows resistance to ammonia and nitriding and carburizing atmosphere. but in the REDOX conditions changed alternately, alloy will be influenced by partial oxidation corrosion media.
Application field is very broad: aircraft engine parts,erosion thermowells in atmosphere,the production and use of caustic alkali metal field,especially the use of sulfur in the environment,the heat treatmen furnace retort and components,especially in the carbide and nitride atmosphere,petrochemical industry in the production of catalytic regenerator and reactor,etc.